Abstract
2.6-4.0 μm continuously wavelength tunable all-solid-state OPO was developed for MALDI. We demonstrated OPO operation with a 2mm-thick MgO: PPSLT with a slope efficiency of 67.2%, which was comparable to 1 mm-thick MgO: PPSLT.
© 2004 Optical Society of America