Abstract

This manuscript describes a simple process for fabricating gold-based, multi-layered, surface-enhanced Raman scattering (SERS) substrates that can be applied to a variety of different nanostructures, while still providing multi-layer enhancement factors comparable to those previously achieved only with optimized silver/silver oxide/silver substrates. In particular, gold multi-layered substrates generated by atomic layer deposition (ALD) have been fabricated and characterized in terms of their optimal performance, revealing multi-layer enhancements of 2.3-fold per spacer layer applied. These substrates were fabricated using TiO₂ as the dielectric spacer material between adjacent gold layers, with ALD providing a conformal thin film with high surface coverage and low thickness. By varying the spacer layer thicknesses from sub-monolayer (non-contiguous) films through multiple TiO₂ layer thick films, the non-monotonic spacer layer thickness response has been elucidated, revealing the importance of thin, contiguous dielectric spacer layers for optimal enhancement. Furthermore, the extended shelf life of these gold multi-layered substrates was characterized, demonstrating usable lifetimes (i.e. following storage in ambient conditions) of greater than five months, with the further potential for simple limited electrochemical regeneration even after this time.

© 2016 The Author(s)

Surface regeneration and signal increase in surface-enhanced Raman scattering substrates

Mikella E. Farrell, Pietro Strobbia, Paul M. Pellegrino, and Brian Cullum
Appl. Opt. 56(3) B198-B213 (2017)

Gold nanorings as substrates for surface-enhanced Raman scattering

Mohamad G. Banaee and Kenneth B. Crozier
Opt. Lett. 35(5) 760-762 (2010)

Surface-enhanced Raman scattering by composite structure of gold nanocube-PMMA-gold film

Xiangxian Wang, Xuelin Bai, Zhiyuan Pang, Jiankai Zhu, Yuan Wu, Hua Yang, Yunping Qi, and Xiaolei Wen
Opt. Mater. Express 9(4) 1872-1881 (2019)

Wafer scale fabrication of highly dense and uniform array of sub-5 nm nanogaps for surface enhanced Raman scatting substrates

Hongbing Cai, YuKun Wu, Yanmeng Dai, Nan Pan, Yangchao Tian, Yi Luo, and Xiaoping Wang
Opt. Express 24(18) 20808-20815 (2016)

Controlling surface enhanced Raman scattering using grating-type patterned nanoporous gold substrates

Yang Jiao, Judson D. Ryckman, Dmitry S. Koktysh, and Sharon M. Weiss
Opt. Mater. Express 3(8) 1137-1148 (2013)