Abstract

The optical properties and stress in thin films of aluminum nitride have been studied as a function of ion energy and the ion-to-vapor arrival ratio (J_i/J_v) for the N₂⁺ ion-assisted deposition of aluminum. The ion energy was varied between 75 and 1000 eV. The refractive index was found to depend on the ion energy and flux. The highest index was 2.10 at 633 nm. The films were found to be highly transparent over the wavelength region 275–800 nm. The films were found to be free of major oxide contamination, and x-ray photoelectron spectroscopy studies revealed the presence of excess nitrogen in films prepared at high J_i/J_v values. The film stress was also found to be related to the ion energy, and an anomalously high compressive stress of −5.0 GPa was found for 100-eV N₂⁺-assisted depositions. By comparison, films prepared by magnetron deposition were found to have lower refractive indices (1.97–1.99, n₆₃₃) and higher stress (−8 to −12 GPa) when deposited in pure nitrogen.

© 1992 Optical Society of America

Optical properties and residual stress in aluminum nitride films prepared by alternating-current dual reactive magnetron sputtering

Chien-Jen Tang, Cheng-Chung Jaing, Kun-Hsien Lee, and Cheng-Chung Lee
Appl. Opt. 50(13) 1945-1950 (2011)

Reactive ion assisted deposition of aluminum oxynitride thin films

Chang Kwon Hwangbo, Linda J. Lingg, John P. Lehan, H. Angus Macleod, and F. Suits
Appl. Opt. 28(14) 2779-2784 (1989)

Effects of low substrate temperature and ion assisted deposition on composition, optical properties, and stress of ZnS thin films

Judith A. Ruffner, Marc D. Himel, Victor Mizrahi, George I. Stegeman, and Ursula J. Gibson
Appl. Opt. 28(24) 5209-5214 (1989)

Effects of bombardment on optical properties during the deposition of silicon nitride by reactive ion-beam sputtering

M. F. Lambrinos, R. Valizadeh, and J. S. Colligon
Appl. Opt. 35(19) 3620-3626 (1996)

Effect of thermal annealing on the optical properties and residual stress of TiO₂ films produced by ion-assisted deposition

Cheng-Chung Lee, Hsi-Chao Chen, and Cheng-Chung Jaing
Appl. Opt. 44(15) 2996-3000 (2005)