In the Twyman effect (1905), when one side of a thin plate with both sides polished is ground, the plate bends: The ground side becomes convex and is in a state of compressive residual stress, described in terms of force per unit length (Newtons per meter) induced by grinding, the stress (Newtons per square meter) induced by grinding, and the depth of the compressive layer (micrometers). We describe and correlate experiments on optical glasses from the literature in conditions of loose abrasive grinding (lapping at fixed nominal pressure, with abrasives 4–400 μm in size) and deterministic microgrinding experiments (at a fixed infeed rate) conducted at the Center for Optics Manufacturing with bound diamond abrasive tools (with a diamond size of 3–40 μm, embedded in metallic bond) and loose abrasive microgrinding (abrasives of less than 3 μm in size). In brittle grinding conditions, the grinding force and the depth of the compressive layer correlate well with glass mechanical properties describing the fracture process, such as indentation crack size. The maximum surface residual compressive stress decreases, and the depth of the compressive layer increases with increasing abrasive size. In lapping conditions the depth of the abrasive grain penetration into the glass surface scales with the surface roughness, and both are determined primarily by glass hardness and secondarily by Young’s modulus for various abrasive sizes and coolants. In the limit of small abrasive size (ductile-mode grinding), the maximum surface compressive stress achieved is near the yield stress of the glass, in agreement with finite-element simulations of indentation in elastic–plastic solids.
© 1996 Optical Society of America
Full Article | PDF ArticleMore Like This
John C. Lambropoulos, Tong Fang, Paul D. Funkenbusch, Stephen D. Jacobs, Michael J. Cumbo, and Donald Golini
Appl. Opt. 35(22) 4448-4462 (1996)
John C. Lambropoulos, Su Xu, and Tong Fang
Appl. Opt. 36(7) 1501-1516 (1997)
James B. Johnson, Robert E. Parks, and James H. Burge
Appl. Opt. 51(18) 4151-4156 (2012)