Abstract

Microporous and macro-mesoporous silicon templates for surface-enhanced Raman scattering (SERS) substrates were produced by anodization of low doped p-type silicon wafers. By immersion plating in AgNO₃, the templates were covered with silver metallic film consisting of different silver nanostructures. Scanning electron microscopy (SEM) micrographs of these SERS substrates showed diverse morphology with significant difference in an average size and size distribution of silver nanoparticles. Ultraviolet-visible-near-infrared (UV-Vis-NIR) reflection spectroscopy showed plasmonic absorption at 398 and 469 nm, which is in accordance with the SEM findings. The activity of the SERS substrates was tested using rhodamine 6G (R6G) dye molecules and 514.5 nm laser excitation. Contrary to the microporous silicon template, the SERS substrate prepared from macro-mesoporous silicon template showed significantly broader size distribution of irregular silver nanoparticles as well as localized surface plasmon resonance closer to excitation laser wavelength. Such silver morphology has high SERS sensitivity that enables ultralow concentration detection of R6G dye molecules up to 10⁻¹⁵ M. To our knowledge, this is the lowest concentration detected of R6G dye molecules on porous silicon-based SERS substrates, which might even indicate possible single molecule detection.

High-performance 3D flexible SERS substrate based on graphene oxide/silver nanoparticles/pyramid PMMA

Xianwu Xiu, Yu Guo, Chonghui Li, Zhen Li, Dazhen Li, Chuanwei Zang, Shouzhen Jiang, Aihua Liu, Baoyuan Man, and Chao Zhang
Opt. Mater. Express 8(4) 844-857 (2018)

Enhanced Raman scattering in porous silicon grating

Jiajia Wang, Zhenhong Jia, and Changwu Lv
Opt. Express 26(6) 6507-6518 (2018)

SERS detection of R6G based on a novel graphene oxide/silver nanoparticles/silicon pyramid arrays structure

C Zhang, S Z Jiang, Y Y Huo, A H Liu, S C Xu, X Y Liu, Z C Sun, Y Y Xu, Z Li, and B Y Man
Opt. Express 23(19) 24811-24821 (2015)

High-performance surface-enhanced Raman scattering substrate prepared by self-assembling of silver nanoparticles into the nanogaps of silver nanoislands

Jiamin Quan, Yong Zhu, Jie Zhang, Junyin Li, and Ning Wang
Appl. Opt. 56(20) 5751-5760 (2017)

Umbrella-frame silicon nanorod arrays decorated with Au nanoparticles as recyclable SERS substrates

Zekun Liao, Xiaofeng Hu, Jiao Chu, Yu Wu, Te Ji, Huachun Zhu, Weiwei Peng, Jie Wang, Hongwei Zhao, and Min Chen
Opt. Express 31(15) 25230-25244 (2023)