Abstract
The fabrication and characteristics of 1.3-µm InGaAsP strain-compensated multiquantum well (SCMQW) buried heterostructure (BH) laser diodes (LDs) grown by selective metal-organic chemical vapor epitaxy on a patterned InP substrate are demonstrated. The photoluminescence (PL) of the SCMQW active region grown on the patterned grooves has a narrow full-width at half-maximum of \sim 47 meV. The BH LDs exhibit a threshold current of 6.8 mA, a slope efficiency of 0.45 mW/mA, and a light output power exceeding 30 mW at 80 mA and 20 °C.. The maximum operating temperature is 120 °C. with a characteristic temperature of 72 K in 20 °C.-80 °C.. The 3-dB modulation bandwidth can be extended as far as 11.4 GHz under a bias level of 40 mA, and the back-to-back tests show a clear and symmetric eye diagram at 10 Gb/s with a PRBS of 231 -1 word length and a peak-to-peak voltage of 1.08 V at 85 °C.. The average increase in operational current is smaller than 0.84% after the 1500-h aging test. The mean time of the BH LDs operated at 85 °C. to fail is calculated as 9 × 104h. These BH LDs satisfy the reliability requirement for strict loop environment and 10-Gb Ethernet application without special hermetic packaging.
© 2006 IEEE
PDF Article
More Like This
Cited By
You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an Optica member, or as an authorized user of your institution.
Contact your librarian or system administrator
or
Login to access Optica Member Subscription