Abstract

Nanoindentation technique was employed to measure the changes in mechanical properties of a glass preform subjected to different levels of UV exposure. The results reveal that short-term exposure leads to an appreciable increase in the Young’s modulus (E), suggesting the densification of the glass, confirming the compaction–densification model. However, on prolonged exposure, E decreases, which provides what we believe to be the first direct evidence of dilation in the glass leading into the Type IIA regime. The present results rule out the hypothesis that continued exposure leads to an irreversible compaction and prove that index modulation regimes are intrinsic to the glass matrix.

© 2009 Optical Society of America

Photoinduced absorption change in germanosilicate preforms: evidence for the color-center model of photosensitivity

L. Dong, J. L. Archambault, L. Reekie, P. St. J. Russell, and D. N. Payne
Appl. Opt. 34(18) 3436-3440 (1995)

Excimer-laser-induced densification in binary silica glasses

N. F. Borrelli, C. M. Smith, and D. C. Allan
Opt. Lett. 24(20) 1401-1403 (1999)

Correlation of defect centers with a wavelength-dependent photosensitive response in germania-doped silica optical fibers

Kelly D. Simmons, Sophie LaRochelle, Victor Mizrahi, George I. Stegeman, and David L. Griscom
Opt. Lett. 16(3) 141-143 (1991)

Direct measurement of 248- and 193-nm excimer-induced densification in silica–germania waveguide blanks

Nicholas F. Borrelli, Douglas C. Allan, and Robert A. Modavis
J. Opt. Soc. Am. B 16(10) 1672-1679 (1999)

Contribution of photoinduced densification to refractive-index modulation in Bragg gratings written in Ge-doped silica fibers

A. I. Gusarov and D. B. Doyle
Opt. Lett. 25(12) 872-874 (2000)