Abstract
We report on the first, to the best of our knowledge, continuous-wave laser operation of a Tm3+,Ho3+-codoped calcium fluoride crystal at ∼2.1 µm. Tm,Ho:CaF2 crystals were grown by the Bridgman method, and their spectroscopic properties were studied. The stimulated-emission cross section for the 5I7 → 5I8 Ho3+ transition is 0.72 × 10−20 cm2 at 2025 nm, and the thermal equilibrium decay time is 11.0 ms. A 3 at. % Tm, 0.3 at. % Ho:CaF2 laser generated 737 mW at 2062–2088 nm with a slope efficiency of 28.0% and a laser threshold of 133 mW. Continuous wavelength tuning between 1985 and 2114 nm (tuning range: 129 nm) was demonstrated. The Tm,Ho:CaF2 crystals are promising for ultrashort pulse generation at ∼2 µm.
© 2023 Optica Publishing Group
Full Article | PDF ArticleMore Like This
Patrick Forster, Clément Romano, Julian Schneider, Marc Eichhorn, and Christelle Kieleck
Opt. Lett. 47(10) 2542-2545 (2022)
Zhen Zhang, Xinsheng Guo, Jingya Wang, Cheng Zhang, Jie Liu, and Liangbi Su
Opt. Lett. 43(17) 4300-4303 (2018)
Zichen Bai, Zhixiang Chen, Yujie Xiong, Hongliang Liu, Siying Gao, Yingying Ren, Xingjuan Zhao, Fengqin Liu, Yuechen Jia, and Feng Chen
Opt. Lett. 49(8) 1977-1980 (2024)