The laser damage resistance of coatings in high-power laser systems depends significantly on the surface quality of the substrate. In our experiment, pits were precisely fabricated on the surface of fused silica substrate using a femtosecond laser processing bench. The high-reflective coatings at 1064 nm were deposited by conventional e-beam evaporation onto fused silica substrates with and without pits, respectively. The internal crack that was induced by the substrate geometrical structure was first observed in our experiment. The laser-induced damage threshold test showed negative effects of the substrate pits on the laser resistance of high-reflective coatings. Simulations by the finite element method were carried out, and results demonstrated that the modulation of a high reflector multilayer geometry could lead to electrical-field amplification and reduce laser damage resistance. Combined with its poor mechanical properties, the pits on substrate could contribute to the occurrence of damages.
© 2015 Optical Society of America
Full Article | PDF ArticleMore Like This
Yingjie Chai, Meiping Zhu, Huanbin Xing, Hu Wang, Yun Cui, and Jianda Shao
Opt. Lett. 41(15) 3403-3406 (2016)
Yingjie Chai, Meiping Zhu, Kui Yi, Weili Zhang, Hu Wang, Zhou Fang, Zhengyuan Bai, Yun Cui, and Jianda Shao
Opt. Lett. 40(16) 3731-3734 (2015)
Huanbin Xing, Meiping Zhu, Yingjie Chai, Kui Yi, Jian Sun, Yun Cui, and Jianda Shao
Opt. Lett. 41(6) 1253-1256 (2016)