Abstract
In this contribution, we report on what we believe to be the first demonstration of an Yb:YAl3(BO3)4 (Yb:YAB) thin-disk laser. Due to its broad gain bandwidth of >40 nm (σ-polarization), Yb:YAB offers the potential for generating ultrafast laser pulses with sub-100-fs durations [1]; the thin-disk geometry should allow to scale the average power of such pulses beyond the 100 W range. For these experiments, Yb:YAB boule material with a doping concentration of 12 % was polished to a disk with a diameter of 6.3 mm and a thickness of 250 μm. The thin-disk crystal was glued with its HR coated backside on a copper heat sink. Although the Yb:YAB crystal was damaged during the mounting process, an usable optical aperture of the disk of up to 3 mm remained. For this reason pump spot diameters of 2.3 and 2.6 mm were selected for the high power laser experiments. A fiber-coupled laser diode (core diameter 600 μm, N.A. 0.22) at a central wavelength of 976 nm emitting up to 1 kW of power was utilized as the pump source. In order to guarantee sufficient pump light absorption, a pump module allowing 24 passes of the pump radiation through the thin-disk was chosen. During laser operation the thin-disk crystal was efficiently cooled by an impingement cooling operated at a water temperature of 15 °C. Prior to the high power experiments a thermal characterization of this thin-disk crystal with a thermal-imaging camera was performed. The temperature of the front side of the crystal was measured both during fluorescence and laser operation. For a pump power density of 2.7 kW/cm2 the maximum surface temperatures was determined to be 71 °C in fluorescence and 56 °C in laser operation. These values confirmed the good suitability of Yb:YAB for high-power laser operation in thin-disk configuration.
© 2013 IEEE
PDF ArticleMore Like This
Junhai Liu, Uwe Griebner, Valentin Petrov, Huaijin Zhang, Jing Li, and Jiyang Wang
CTuKK2 Conference on Lasers and Electro-Optics (CLEO:S&I) 2008
Christian Kränkel, Rigo Peters, Klaus Petermann, and Günter Huber
MF5 Advanced Solid-State Photonics (ASSL) 2008
Junhai Liu, Xavier Mateos, Valentin Petrov, Huaijin Zhang, Jing Li, and Jiyang Wang
CFJ7 Conference on Lasers and Electro-Optics (CLEO:S&I) 2007