Abstract
We propose a novel surface-plasmon-resonance sensor design based on coating the holes of a three-hole microstructured optical fiber with a low-index dielectric layer on top of which a gold layer is deposited. The use of all three fiber holes and their relatively large size should facilitate the fabrication of the inclusions and the infiltration of the analyte. Our numerical results indicate that the optical loss of the Gaussian guided mode can be made very small by tuning the thickness of the dielectric layer and that the refractive-index resolution for aqueous analytes is 1×10-4.
©2008 Optical Society of America
1. Introduction
Quite recently, Sazio et al. [1] demonstrated that high-pressure chemical deposition techniques can be used to uniformly coat the hole surfaces of a microstructured optical fiber (MOF) with a variety of materials, e.g., with gold. Later on, the excitation of plasmon resonances in MOFs with coated metal inclusions have actively been studied using both experimental [2, 3] and numerical [4, 5, 6, 7] methods. The resonance wavelength of the plasmon excitation strongly depends on the dielectric function of the material in contact with the metal. Owing to this characteristic, compact fiber-optic surface-plasmon-resonance (SPR) sensors for liquid substances can be constructed by infiltrating the analyte into the metal-coated holes of the MOF. The refractive index of the analyte can then be retrieved either by measuring the transmission spectrum or by monitoring the transmitted power at certain wavelength. So far, numerical analyses of such MOF-integrated SPR sensors based on both index-guiding [5, 6] and bandgap-guiding [7] fibers have been reported. In these proposed designs, however, selective coating and filling of the fiber holes are required.
In this paper, we propose a novel SPR sensor design based on coating the inner surfaces of a three-hole MOF with a dielectric layer on top of which a gold layer is deposited. The use of all three fiber holes along with their notably large size should facilitate the fabrication of the inclusions and the infiltration of the analyte. The low-index dielectric is sandwiched between the original MOF and a thin layer of gold to control the overlap between the fundamental core mode and the gold coating. We investigate numerically the excitation of plasmon resonances in the proposed sensor fiber. Three-hole MOFs, also termed suspended-core fibers, have previously been applied mainly in evanescent-wave sensing [8, 9] but also in dispersion management [10] and in the construction of a fiber Bragg grating refractometer [11].
This paper is organized as follows. In Section 2, we detail the proposed design and the numerical modeling procedure. The dependence of the plasmon-resonance loss spectrum on the essential design parameters is characterized in Section 3. The paper is summarized and concluded with a discussion in Section 4.
2. Sensor design and numerical modeling
We start by considering a three-hole MOF, such as the one shown in Fig. 1(a). For sensor operation, the hole surfaces are first uniformly coated with an auxiliary dielectric layer of thickness s. The layer is assumed to have a lower refractive index than that of the original MOF to provide mode confinement. Then, on top of this auxiliary layer, a gold layer of thickness d is deposited. The cross section of the resulting structure is schematically depicted in Fig. 1(b). The center of curvature dictating the core shape [point P in Fig. 1(b)] is taken to shape the coated layers as well [1]. Lastly, the fiber holes are assumed to be filled with an aqueous analyte.
The electromagnetic mode of the sensor fiber is solved with the finite element method (FEM) by using COMSOL Multiphysics software [12]. For the FEM modeling, we fix the radius of curvature to r=4 µm and the thickness of the core struts to c=200 nm. The refractive indices of the original MOF and the low-index layer are chosen to roughly correspond to doped silica. For gold, we use the tabulated refractive-index values [13] with linear interpolation between the data points. To reduce the computation time, we assume that only the core and its struts are coated. Furthermore, only one half of the structure needs to be considered thanks to its symmetry properties [14]. Halving of the structure gives rise to an artificial boundary which is taken to be either a perfect magnetic conductor (PMC) or a perfect electric conductor (PEC). The corresponding boundary conditions are written as n×H=0 and n×E=0, respectively, with n being a unit vector perpendicular to the boundary and H (E) denoting the magnetic (electric) field. At the remaining outer border, a perfectly matched layer is chosen to handle the boundary condition. Figure 1(c) shows an example FEM mesh along with the boundary conditions at the borders of the computing region. Within the computing region, continuity of the tangential field components across the material boundaries is assumed.
In order to find the propagating mode of the sensor, we solve the vector wave equation
with the following ansatz
Here, ε describes the relative, complex dielectric function, k 0=2π/λ is the wavenumber with λ being the free-space wavelength, ω is the angular frequency of light, and t denotes time. The propagation constant can be expressed as
where n eff is the effective index of the mode. The decay in the power of the mode as it propagates through the sensor fiber (toward the positive z direction) can be described with the formula
where P 0 is the power at the plane z=0. The attenuation constant α is proportional to the imaginary part of the effective index according to the relation
We use the parameter α to quantify the propagation loss of the Gaussian guided modes which are obtained by using either the PMC or the PEC boundary conditions. These modes are degenerate within the accuracy of our computations.
3. Results
The modal propagation loss peaks at the plasmon-resonance wavelength which depends not only on the analyte but also on the thickness of the gold layer. Figure 2(a) shows the modal loss as a function of wavelength for different thicknesses of the gold layer. The thickness of the dielectric layer is fixed to s=1.5 µm and the refractive indices of the original MOF, the dielectric layer, and the analyte are taken to be nc=1.46, ns=1.44, and na=1.33, respectively. The sharp bends in the curves near λ=564 nm originate from the use of the tabulated refractive-index data for gold. Consequently, we fix the gold layer thickness to d=30 nm in our further calculations to clearly distinguish the plasmon resonance. Figure 2(b) illustrates the spatial characteristics of the mode (here s=1 µm and λ=530 nm). The mode is very close to Gaussian in its overall shape throughout the loss peak. At the interface between the gold and the analyte, however, the field amplitude locally decays in both of the materials, which is a characteristic of plasmon excitation.
The plasmon amplitude and thus the overall loss of the sensor can be tuned to a tolerable level by selecting the layer thickness s appropriately. This is exemplified in Fig. 3(a) which shows the modal loss spectrum for several values of the parameter s. Two values, na=1.33 and na=1.34, are used for the refractive index of the analyte to assess the refractive-index resolution. The other refractive indices are taken to be nc=1.46 and ns=1.44. The peak wavelength and the analyte-dependent shift in the resonance peak, Δλ peak, are identical for all values of s. Thus, the thickness-parameter s lends itself well to exclusively controlling the overall loss.
On the other hand, if the refractive index of the core is varied, as in Fig. 3(b), both the peak wavelength and the analyte-dependent shift Δλ peak will change. Here, we have fixed the parameters s=1.5 µm and ns=1.44. The peak shift is at its strongest when the parameter nc is in value close to ns. In such a case, the small refractive-index contrast between the core and the auxiliary dielectric limits the number of core-confined modes. In particular, by choosing a small-core MOF to begin with, the device can be made to support a single transverse mode throughout the resonance peak. To estimate the required core dimension, we crudely approximate our sensor waveguide with a conventional step-index fiber that has an index contrast equal to Δn=nc-ns=0.01. In such a case, the effective core radius, calculated through the V parameter [15], would have to be smaller than 1.1 µm. The dimensions in our design [see Fig. 1(c)] are on this order.
By measuring the transmission spectrum of the sensor fiber, refractive-index resolution of
can be attained by choosing nc=1.45. Here, the parameter Δna=0.01 is the difference in the refractive indices of the two analytes, and the peak shift is estimated from Fig. 3(b) to be Δλ peak ≈ 10 nm. The instrumental peak-wavelength resolution is assumed to be Δλ min=0.1 nm. In another approach, the transmitted optical power is monitored at a fixed wavelength. For this operation mode, it is useful to introduce a sensitivity parameter [5]
This parameter is valid for a sensor of length 1/α 1.33, with α 1.33 denoting the modal loss for the case na=1.33. Figure 4 shows the sensitivity S as obtained from the data of Fig. 3(b). By using the data of Fig. 3(a), we confirm that these sensitivity curves do not depend on the value of the parameter s which can also in this operation mode be used to exclusively control the loss. If one assumes that a 1% change in the transmitted power can reliably be measured [5], refractive-index changes on the order of 10-4 (for S ≈ 80) could be detected with this configuration.
4. Summary and discussion
We have proposed a novel surface-plasmon-resonance sensor design based on coating a three-hole MOF with a dielectric layer on top of which a gold layer is deposited. The presented design has the following advantages. First, the holes of the three-hole MOF can be tens of micrometers in diameter, which should facilitate the fabrication of the layered sensor structure and the infiltration of the analyte. Second, a single design parameter can be used to tune the loss level of the sensor without affecting the other plasmon-resonance characteristics. Third, the sensor can be made to support a single transverse mode which is essentially Gaussian in shape. Finally, the refractive-index resolution is estimated to be 1×10-4 which is comparable to the figure given in Ref. [5].
We remark that the first fabrication step, i.e., the production of the auxiliary dielectric layer, could alternatively be done by using the usual stack-and-draw technique. For instance, in Ref. [16], this technique was used with an appropriate preform to produce annular up-doped layers (within a hexagonal lattice). We believe that this approach could also be used with three-hole MOFs to produce down-doped, low-index layers on the hole surfaces. Yet another approach would be to use a three-hole MOF with an up-doped core, similar to the one presented in Ref. [11]. This way, one could attain efficient mode confinement for controlling the modal loss without using a separate low-index dielectric layer. In closing, we note that besides gold, also copper was found to exhibit a clearly distinguishable plasmon resonance in the course of our numerical investigations.
Acknowledgments
This work has been funded by the Academy of Finland (project nos. 210777 and 124165). Part of the work was conducted within the COST 299 - Fides. Additionally, M. Hautakorpi acknowledges the Finnish Cultural Foundation for funding in the early stages of this research.
References and links
1. P. J. A. Sazio, A. Amezcua-Correa, C. E. Finlayson, J. R. Hayes, T. J. Scheidemantel, N. F. Baril, B. R. Jackson, D.-J. Won, F. Zhang, E. R. Margine, V. Gopalan, V. H. Crespi, and J. V. Badding, “Microstructured optical fibers as high-pressure microfluidic reactors,” Science 311, 1583–1586 (2006). [CrossRef]
2. X. Zhang, R. Wang, F. Cox, B. T. Kuhlmey, and M. C. J. Large, “Selective coating of holes in microstructured optical fiber and its application to in-fiber absorptive polarizers,” Opt. Express 15, 16270–16278 (2006). [CrossRef]
3. A. Amezcua-Correa, J. Yang, C. E. Finlayson, A. C. Peacock, J. R. Hayes, P. J. A. Sazio, J. J. Baumberg, and S. M. Howdle, “Surface-enhanced Raman scattering using microstructured optical fiber substrates,” Adv. Funct. Mater. 17, 2024–2030 (2007). [CrossRef]
4. B. T. Kuhlmey, K. Pathmanandavel, and R. C. McPhedran, “Multipole analysis of photonic crystal fibers with coated inclusions,” Opt. Express 14, 10851–10864 (2006). [CrossRef] [PubMed]
5. A. Hassani and M. Skorobogatiy, “Design of the microstructured optical fiber-based surface plasmon resonance sensor with enhanced microfluidics,” Opt. Express 14, 11616–11621 (2006). [CrossRef] [PubMed]
6. A. Hassani and M. Skorobogatiy, “Design criteria for microstructured-optical-fiber-based surface-plasmon-resonance sensors,” J. Opt. Soc. Am. B 24, 1423–1429 (2007). [CrossRef]
7. B. Gauvreau, A. Hassani, M. F. Fehri, A. Kabashin, and M. Skorobogatiy, “Photonic bandgap fiber-based surface plasmon resonance sensors,” Opt. Express 15, 11413–11426 (2007). [CrossRef] [PubMed]
8. Y. Ruan, E. P. Schartner, H. Ebendorff-Heidepriem, P. Hoffmann, and T. M. Monro, “Detection of quantum-dot labeled proteins using soft-glass microstructured optical fibers,” Opt. Express 15, 17819–17826 (2007). [CrossRef] [PubMed]
9. S. Afshar V., S. C. Warren-Smith, and T. M. Monro, “Enhancement of fluorescence-based sensing using microstructured optical fibers,” Opt. Express 15, 17891–17901 (2007). [CrossRef]
10. C. M. B. Cordeiro, M. A. R. Franco, C. J. S. Matos, F. Sircilli, V. A. Serrão, and C. H. Brito Cruz, “Single-design-parameter microstructured optical fiber for chromatic dispersion tailoring and evanescent field enhancement,” Opt. Lett. 32, 3324–3326 (2007). [CrossRef] [PubMed]
11. M. C. P. Huy, G. Laffont, V. Dewynter, P. Ferdinand, P. Roy, J. -L. Auguste, D. Pagnoux, W. Blanc, and B. Dussardier, “Three-hole microstructured optical fiber for efficient fiber Bragg grating refractometer,” Opt. Lett. 32, 2390–2392 (2007). [CrossRef]
13. E. D. Palik , ed., Handbook of Optical Constants of Solids (Academic Press, San Diego, Calif., 1998).
14. H. P. Uranus, “A simple and intuitive procedure for evaluating mode degeneracy in photonic crystal fibers,” Am. J. Phys. 74, 211–217 (2006). [CrossRef]
15. G. P. Agrawal, Nonlinear Fiber Optics, 3rd ed. (Academic Press, San Diego, Calif., 2001).
16. S. Kim, Y. Jung, K. Oh, J. Kobelke, K. Schuster, and J. Kirchhof, “Defect and lattice structure for air-silica index-guiding holey fibers,” Opt. Lett. 31, 164–166 (2006). [CrossRef] [PubMed]