Abstract
Electrospun fibers of amorphous or low-crystallinity polymers typically exhibit a low molecular orientation that can hamper their properties and application. A key stage of the electrospinning process that could be harnessed to mitigate the loss of orientation is jet rigidification, which relates closely to the solvent evaporation rate. Here, we establish quantitative Raman methods to assess the molecular orientation and crystallinity of weakly crystalline poly(2,6-dimethyl-1,4-phenylene oxide) fibers with varying diameters. Our findings demonstrate that solvent volatility can be leveraged to modulate the orientation and crystallinity through its impact on the effective glass transition temperature (Tg,eff) of the polymer jet during the electrospinning process. Specifically, a highly volatile solvent yields a higher and more sustained orientation (median 〈P2〉 of 0.53 for diameters < 1.0 µm) because its fast evaporation rapidly increases Tg,eff above room temperature. This vitrification early along the jet path promotes the formation of an oriented amorphous phase and a moderate fraction of strain-induced crystals. Our data reveals that a high Tg is a crucial parameter for reaching high orientation in amorphous or low-crystallinity polymer systems.
© 2023 The Author(s)
PDF Article
More Like This
Cited By
Optica participates in Crossref's Cited-By Linking service. Citing articles from Optica Publishing Group journals and other participating publishers are listed here.
Open Access
Add to BibSonomy