We report on the optical properties of a structurally modified silicate glass doped with Au ions. The area in the vicinity of the focal point of an 800-nm femtosecond laser in a glass sample became gray as a result of the formation of color centers after laser irradiation and turned red because of precipitation of Au nanoparticles after further annealing at 550 °C for 30 min. When the glass was excited by UV light at 365 nm, yellowish-white and orange-yellow emissions were observed in the laser-irradiated and the Au-nanoparticle-precipitated area, respectively. An optical Kerr shutter experiment showed that the Au nanoparticle-precipitated glass had an ultrafast nonlinear optical response, and the third-order nonlinear susceptibility was estimated to be .
© 2004 Optical Society of America
Full Article | PDF ArticleMore Like This
Quan-Zhong Zhao, Jian-Rong Qiu, Xiong-Wei Jiang, Chong-Jun Zhao, and Cong-Shan Zhu
Opt. Express 12(17) 4035-4040 (2004)
Jianrong Qiu, K. Kojima, K. Miura, T. Mitsuyu, and K. Hirao
Opt. Lett. 24(11) 786-788 (1999)
Victor Dubrovin, Nikolay Nikonorov, and Alexander Ignatiev
Opt. Mater. Express 7(7) 2280-2292 (2017)