Abstract
Further power scaling and stable laser performance were demonstrated in the Yb/Ce codoped aluminosilicate fiber fabricated through low-temperature chelate gas phase deposition technique. The molar ratio of Ce/Yb was designed and optimized to be 0.58 for low background loss, effective photodarkening suppression, and no additional thermal load. The background loss of this active fiber was 4.7 dB/km and its photodarkening loss at equilibrium was as low as 3.9 dB/m at 633 nm. Benefiting from low-temperature deposition technique, the fiber showed uniform core composition devoid of clustering and central ‘dip’ of refractive index profile and 0.19 mol% Yb2O3 was homogeneously dissolved into the fiber core plus with 0.41 mol% Al2O3, 0.11 mol% Ce2O3, and 0.32 mol% SiF4. Based on a master oscillator power amplifier laser setup, 5.04 kW laser output at 1079.80 nm was achieved with a slope efficiency of 81.1%. Stabilized at 5kW-level laser for over 60 minutes, the output power presented almost no power degradation, directly confirming a noticeable photodarkening mitigation.
PDF Article
More Like This
Ultra-low-loss double-cladding laser fiber fabricated by optimized chelate gas phase deposition technique
Shengfei She, Weinan Li, Chang Chang, Zhe Li, Jinkun Zheng, Song Gao, Yan Zhang, Gang Li, Qi Gao, Wei Zhao, Baoyin Zhao, Haitao Guo, and Chaoqi Hou
Appl. Opt. 57(27) 7943-7949 (2018)
Multi-kW Yb-doped aluminophosphosilicate fiber
Shuang Liu, Huan Zhan, Kun Peng, Yuwei Li, Shihao Sun, Jiali Jiang, Li Ni, Xiaolong Wang, Juan Yu, Lei Jiang, Rihong Zhu, Jianjun Wang, Feng Jing, and Aoxiang Lin
Opt. Mater. Express 8(8) 2114-2124 (2018)
Cited By
You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an Optica member, or as an authorized user of your institution.
Contact your librarian or system administrator
or
Login to access Optica Member Subscription