Abstract
In this paper, a hydrothermal method is used to synthesize a nickel oxide nanostructure (nano-NiO) for its application to inverted perovskite solar cells. These pore nanostructures were employed to increase both the contact and channel between the hole transport and perovskite layers of an ITO/nano-${\rm NiO}/{{\rm CH}_3}{{\rm NH}_3}{{\rm PbI}_3}/{\rm PCBM}/{\rm Ag}$ device. The purpose of this research is twofold. First, three different nano-NiO morphologies were synthesized at temperatures of 140°C, 160°C, and 180°C. Then, a Raman spectrometer was used to check the phonon vibration and magnon scattering characteristics after an annealing temperature of 500°C. Second, nano-NiO powders were dispersed in isopropanol for subsequent spin coating on the inverted solar cells. The nano-NiO morphologies were multi-layer flakes, microspheres, and particles at synthesis temperatures of 140°C, 160°C, and 180°C, respectively. When the microsphere nano-NiO was used as the hole transport layer, the perovskite layer had a larger coverage of 83.9%. The grain size of the perovskite layer was analyzed by x-ray diffraction, and strong crystal orientations of (110) and (220) peaks were found. Despite this, the power conversion efficiency could affect the promotion, which is 1.37 times higher than the poly(3,4-ethylenedioxythiophene) polystyrene sulfonate element conversion efficiency of the planar structure.
© 2023 Optica Publishing Group
Full Article | PDF ArticleMore Like This
Chengyi Duan, Xiaofei Zhang, Zheren Du, Jia Chen, Ramy El-Bashar, S. S. A. Obayya, Mohamed Hameed, and Jun Dai
Opt. Express 31(12) 20364-20376 (2023)
Ming-Hua Liu, Zheng-Ji Zhou, Pan-Pan Zhang, Qing-Wen Tian, Wen-Hui Zhou, Dong-Xing Kou, and Si-Xin Wu
Opt. Express 24(22) A1349-A1359 (2016)
Fei Zhao, Yixin Guo, Jiahua Tao, Zeng Li, Jinchun Jiang, and Junhao Chu
Appl. Opt. 59(18) 5481-5486 (2020)